20.500.12556/DKUM-26033 Localized dissolution kinetics of low carbon steel Localized dissolution of low carbon steel in saturated calcium hydroxide with different amount of sodium chloride has been investigated, using a dc technique. Potentiokinetic polarization curves indicated that pitting potentials ($E_{pit}$) decrease linearly with the log of chloride concentration. The rate of pit nucleation (1/$t_i$), and the rate of pits growth increases with increasing concentration of $Cl^-$ ions. Initiation of pitting attack could be ascribed to the adsorption of $Cl^-$ ions on the oxide surface. Adsorption of $Cl^-$ ions is physisorption and follow the Langmuir isotherm with $Δ_{ads}G^0$ = -21.1 kJ/mol. S pomočjo dc tehnike smo raziskovali lokalizirano raztapljanje malo-ogljičnega jekla v nasičeni raztopini kalcijevega hidroksida ob dodanih različnih množinah natrijevega klorida. Poteciokinetične polarizacijske krivulje so pokazale, da se kritični porušitveni potencial ($E_{pit}$) linearno zmanjšuje z logaritmom koncentracije kloridnih ionov. Hitrost nastajanja luknjic (1/$t_i$) in hitrost rasti luknjic se povečuje s povečanjem koncentracije $Cl^–$ ionov. Iniciacijo točkaste poškodbe lahko pripišemo adsorpciji $Cl^–$ ionov na oksidno površino. Adsorpcija $Cl^–$ je fizisorpcija in sledi Langmuirjevi adsorpcijski izotermi z $∆_{ads}G^0$ = –21.1 kJ/mol. pitting corrosion adsorption isotherm low carbon steel simulated interstitial solution točkasta korozija adsorpcijska izoterma nizkoogljična jekla true false true Angleški jezik Slovenski jezik Znanstveno delo 2012-05-31 11:44:31 2012-05-31 11:44:31 2022-04-15 13:18:58 2023-12-31 03:31:36 2007 0 0 str. 725-729 št. 4 Letn. 54 0000-00-00 Zaloznikova Objavljeno NiDoloceno 0000-00-00 0000-00-00 0000-00-00 1318-0207 544.431 14086149 11991318 1318-0207 URN:SI:UM:DK:TBXERCZT Acta_Chimica_Slovenica_2007_Petek,_Dole_Localized_Dissolution_Kinetics_of_Low_Carbon_Steel.pdf Acta_Chimica_Slovenica_2007_Petek,_Dole_Localized_Dissolution_Kinetics_of_Low_Carbon_Steel.pdf 1 F09EF8CE830FA5C30119384D7966F039 bcd484e105be17f3a2b12413385badb58681e72bb0378d04d722ad197821f8b5 1be235fa-7c07-11eb-bb7a-00155d0001ca 20.500.12556/dkum/f2a55272-0b7d-4f1a-9d73-40413e37287e https://dk.um.si/Dokument.php?lang=slv&id=115538 http://acta-arhiv.chem-soc.si/54/54-4-725.pdf 1 https://dk.um.si/Dokument.php?lang=slv&id=34938 Fakulteta za kemijo in kemijsko tehnologijo 0 0 0