20.500.12556/DKUM-26568 Bond improvement in cementitious mortars reinforced with continuous carbon filaments Among various parameters that influence the properties of the composite, the bond between the cementitious matrix and the fibres is the most important one. This paper investigates the influence of admixtures - silica fume, superplasticizer and air entraining agent - on the improvement of the bond between bundled carbon filaments and cementitious mortars. An overall microstructural analysis has shown that the addition of silica fume strengthen the interfacial transition zone by both the reduction of its porosity and the consumption of CH crystals. The addition of a superplasticizer increased the workability of fresh mortars, but the bond improvement was insignificant. The application of the air entraining agent caused the formation of air bubbles inside the mortar matrix. Air bubbles formed in the vicinity of the multifilament yarn were found to provide mechanical anchoring for fibres leading to a significant increase in interface friction. Fibre-bundle pullout tests were carried out to confirm the effectiveness of the admixtures to improve the interface bonding. Based on the resulting load-displacement curves, air entraining agent was found to be most effective in enhancing the bonding characteristics of the cementitious composite. carbon fibers cementitious composites bond properties true false false Angleški jezik Angleški jezik Neznano 2012-05-31 14:01:17 2012-05-31 14:01:17 2022-04-15 03:42:04 2024-01-03 03:31:49 2009 0 0 0000-00-00 NiDoloceno NiDoloceno NiDoloceno 0000-00-00 0000-00-00 0000-00-00 691 14199062 1735-5540 URN:SI:UM:DK:LRQAQF8D http://www.civilica.com/EnPaper-ICCT01-ICCT01_096.html 1 https://dk.um.si/Dokument.php?lang=slv&id=35626 Fakulteta za gradbeništvo, prometno inženirstvo in arhitekturo 0 0 0