20.500.12556/DKUM-27048 Effect of residual stresses on the fatigue crack propagation in welded joints The effect of residual stress on the fatigue crack growth was investigated forcyclic tension. Three-point bend specimens were used with through thicknessnotches at the center line of the welded joint. The experiments were performed for different load amplitudes and load ratios under conditions of small-scale yielding. The influence of the residual stresses on fatigue crack growth was estimated by experimentally observed fatigue crack growth rate and measurement of residual stresses at the surface of specimen. This paper describes an approach taken in two models to estimate the residual stress effect on fatigue crack propagation and to predict remaining service life of awelded structure. fracture mechnaics fatigue crack crack growth residual stresses fatigue crack growh rate X-ray lomna mehanika utrujenostna razpoka širjenje razpoke zaostale napetosti stopnja rasti razpoke true false false Angleški jezik Angleški jezik Neznano 2012-06-01 09:42:39 2012-06-01 09:42:39 2022-04-15 03:43:19 2019-07-10 12:11:03 2005 0 0 0000-00-00 NiDoloceno NiDoloceno NiDoloceno 0000-00-00 0000-00-00 0000-00-00 539.42:620.17 9785878 Y505-8627 URN:SI:UM:DK:ST1BIYME http://dx.doi.org/10.1520/JAI12036 1 https://dk.um.si/Dokument.php?lang=slv&id=36284 Fakulteta za strojništvo 0 0 0