20.500.12556/DKUM-27561 The characterisation of nanosized nickel-zinc ferrites synthesized within reverse micelles of CTAB/1-hexanol/water microemulsion Stoichiometric nanocrystalline nickel-zinc ferrites were synthesized by a reverse micelle method following a multi-microemulsion approach. Different pH values were chosen for the alkali precipitating reaction during the synthesis of different powders. Synthesized, as-dried and subsequently calcined powders were characterized in terms of their magnetic properties. XRD analyses and specific-surface area measurements were used to determine the average particlesizes of the synthesized samples. DCS and TGA measurements were performed to reveal the phase transitions within the samples at elevated temperatures, whereas TEM was used to view and record the microstructure of the nanosized ferrite samples. A possible mechanism of the formation of the synthesized NiZn-ferrite was also discussed. magnetic materials magnetic nanoparticles microemulsion synthesis nickel iron fine powders Ni-Zn ferrites reverse micelle method magnetni materiali magnetni nanodelci mikroemulzijska sinteza nikelj železo fini prahovi Ni-Zn feriti reverzni micel true false false Angleški jezik Angleški jezik Neznano 2012-06-01 11:38:35 2012-06-01 11:38:35 2022-04-15 03:45:13 2019-07-10 12:19:11 2004 0 0 0000-00-00 NiDoloceno NiDoloceno NiDoloceno 0000-00-00 0000-00-00 0000-00-00 54.057:669.018.9 9327894 0304-8853 URN:SI:UM:DK:XLSOMQYN http://dx.doi.org/10.1016/j.jmmm.2004.06.051 1 https://dk.um.si/Dokument.php?lang=slv&id=36863 Fakulteta za kemijo in kemijsko tehnologijo 0 0 0