20.500.12556/DKUM-39550 Barve in funkcionalne lastnosti materialov Colors and funkcional characteristics of materials Cilj naloge je bil razvoj primernega postopka aplikacije TiO2 delcev na surovem in obarvanem PES materialu, za doseganje dobre UV zaščite in samočistilnega učinka. Za modifikacijo vlaken smo uporabili dve obliki TiO2 nano delcev – rutilno in anatazno, ki so bili različno površinsko modificirani in smo jih na vlakna nanašali z uporabo različnih postopkov. Raziskava je zajemala dva sklopa. V prvem smo raziskovali primernost postopka nanosa sedmih različno površinsko modificiranih TiO2 past – rutilno in anatazno v obliki suspenzij. Za nanos smo uporabili postopek izčrpavanja in postopek impregnacije. Pri postopku izčrpavanja smo želeli ugotoviti tudi kompatibilnost postopka barvanja in istočasnega nanosa past. Za ugotavljanje učinkovitosti postopkov smo primerjali UPF vrednosti surovih, obarvanih in s pastami obdelanih vzorcev in ugotavljali spremembe barve kot posledica uporabe različnih postopkov. Pri postopku impregnacije smo za paste z rutilno obliko TiO2 PES vzorcev impregnirali v koncentracijah 1 g/L, 3 g/L in 5 g/L, drugi del PES vzorcev pa smo impregnirali s pastami, ki vsebujejo anatazno obliko TiO2, in sicer v koncentracijah 5 g/L, 10 g/L in 30 g/L. Fiksiranje je potekalo pri temperaturi 180 °C. Na podlagi analiz tako obdelanih vzorcev, smo ugotavljali učinkovitost nanosa in določili optimalno koncentracijo, ki je glede na dosežene rezultate pri postopku impregnacije 10 g/L, pri postopku izčrpavanja pa 9 %. Pri analizi funkcionalnih lastnosti smo tako impregnirane vzorce umazali s sokom rdeče pese in z rdečim vinom. Vzorce smo v različnih časovnih intervalih osvetljevali z dnevno svetlobo in v komori z UV svetlobo. Rezultati raziskave so pokazali, da lahko uporabimo tako izčrpalni kot impregnacijski način nanosa različnih past, da sta postopek barvanja in nanosa kompatibilna, da nam tovrstni nanosi dajejo dobro zaščito pred UV žarki, da pa je njihova samočistilnost omejena le na določene madeže. The aim of the presented work was to develop a suitable process for TiO2 application on dyed and raw PES materials, in order to attain excellent UV protective and self-cleaning properties. Polyester fibres were used for the research purpose. For surface modification, two types of nano TiO2 forms were used – rutile and anatase and applied on polyester fibres by different techniques. The research was composed of two phases. Firstly, the appropriate application procedure for coating of seven nano TiO2 colloidal suspensions (rutile and anatase form) was studied, i.e. exhaustion and impregnation. During the exhaustion procedure, disperse dye stuffs were also included.UPF values were determined on dyed and/or TiO2 treated samples. During the impregnation procedure, various concentration of TiO2 colloidal suspension were applied (1, 3, 5, 10 and 30 g/L), and curing temperature was used (180 °C), with the intention to determine the optimal application conditions along with the maximal amount of TiO2. Secondly, the impregnated samples were spotted with two stains, i.e. red beet and red wine, and there after illuminated for 160 hours under daylight as well as in the chamber equipped with an artificial UV light. The obtained results show that above mentioned applications give excellent protection against UV rays, although the self-cleaning of modified fabrics does not achieve desired values. UV zaščita poliester disperzna barvila TiO2 nanodelci samočistilnost UV protection polyester disperse dyestuffs TiO2 nanoparticles self-cleaning true true false [M. Blagovič] Slovenski jezik Angleški jezik Magistrsko delo 2013-01-29 12:22:19 2013-02-05 13:44:55 2022-05-12 23:02:12 2021-04-22 03:17:29 2013 0 Maribor 0 0000-00-00 NiDoloceno NiDoloceno NiDoloceno 0000-00-00 0000-00-00 0000-00-00 535.66:677.027(043) 17546006 URN:SI:UM:DK:X0YJCM0B MAG_Blagovic_Mateja_2013.pdf MAG_Blagovic_Mateja_2013.pdf 1 63AD7F45F91CEA15587CCDCE91E2142C 1004ea7f35c6c4edba810556a80b3e74cbcbd308100cfe5a9f96fd28df9de892 2750eaf8-7c09-11eb-bb7a-00155d0001ca 20.500.12556/dkum/0bdc3727-ce9c-442e-83f9-f59edc82d94e https://dk.um.si/Dokument.php?lang=slv&id=53550 Fakulteta za strojništvo 0 0 0