20.500.12556/DKUM-47774 OPTIMIZACIJA OPTIČNIH LASTNOSTI DEKORATIVNEGA OMETA ZA NOTRANJO UPORABO OPTIMIZATION OF SYNTHETIC RESIN PLASTER FORMULATION FOR INDOOR USE V diplomskem delu smo optimizirali formulacijo disperznega dekorativnega ometa (NDO) za notranjo uporabo. V raziskavi smo iskali vzrok za nezadostno belino, ki je posledica izrazitega rumenega podtona notranjega dekorativnega ometa. Znani so številni razlogi za pojav rumenega podtona v premazih. V diplomskem delu smo se osredotočili na prispevek titanovega dioksida (TiO2). Na trgu je na voljo veliko različic TiO2, ki se razlikujejo po postopku izdelave, čistosti, površinski obdelavi, velikosti delcev, kristalni strukturi (rutil, anataz), kar vse vpliva tudi na optične lastnosti premaza. V prvem delu diplomskega dela smo optimizirali optične lastnosti NDO z TiO2 rutilne kristalne strukture proizvedenem po sulfatnem postopku. Najprej smo preverili, kako na belino in rumen podton vpliva vsebnost TiO2 v formulaciji. Nato smo ugotavljali, kako na belino in rumen podton vpliva čas dispergiranja. V drugem delu raziskave smo testirali optične lastnosti NDO z drugimi tipi TiO2, in sicer rutilom proizvedenem po kloridnem postopku in anatazom proizvedenem po sulfatnem postopku. V zadnjem delu raziskave smo rumen podton poizkušali izničiti z dodajanjem modrega pigmenta. Optične lastnosti smo merili s spektrofometrom, vzorce pa pregledali tudi vizualno. Vse štiri možnosti smo na koncu primerjali in izbrali ekonomsko in tehnično najprimernejšo rešitev. In this thesis, we optimized formulation of decorative plaster for interior use (DPIU). Reasons for the yellow undertone and hence the lack of whiteness of DPIU were investigated. There are many reasons known for the appearance of a yellow undertone in coatings. In this thesis, we focused on the contribution of titanium dioxide (TiO2). There are many sorts of TiO2 available on the market, which differ in manufacturing process, purity, surface treatment, particle size and crystalline structure, all of which affect the optical properties of the plaster. In the first part of this study rutile type of TiO2 manufactured by sulphate synthesis was investigated. Differences in whiteness and yellow undertone of DPIU caused by different TiO2 content and dispersing time were observed. In second part two alternative types (rutile, chloride synthesis and anatse, sulphate synthesis) of TiO2 were investigated. In the last part of the study we tried to eliminate the yellow undertone by adding blue pigment. The optical properties were measured with a spectrophotometer, and also visually. All four options are finally compared and selected according to economic and technical aspects. belina dekorativni omet TiO2 optične lastnosti podton kolormetrija whiteness decorative plaster TiO2 optical properties undertone colorimetry true true false [M. Dergan] Slovenski jezik Angleški jezik Diplomsko delo/naloga 2015-04-06 23:38:03 2015-04-22 08:13:26 2022-05-23 03:06:14 2021-05-07 03:35:18 2015 0 Maribor 0 0000-00-00 NiDoloceno NiDoloceno NiDoloceno 0000-00-00 0000-00-00 0000-00-00 2018-05-11 667.633.4(043.2) 18667286 URN:SI:UM:DK:4K3EPMVW UN_Dergan_Mihael_2015.pdf UN_Dergan_Mihael_2015.pdf 1 4B5641D799DEB955E2C3E415AF3DF3E2 4ebdad8b529b19eadf6c6910014d4bd2e46c2e266907e1b9eb0cacbdf9f838c7 f4e7f94e-7c07-11eb-bb7a-00155d0001ca https://dk.um.si/Dokument.php?lang=slv&id=71317 Fakulteta za kemijo in kemijsko tehnologijo 0 0 0