20.500.12556/DKUM-49865 Fracture toughness of heterogeneous energy components Lomna žilavost heterogenih energetskih komponent The presence of different microstructures along pre-crack fatigue fronts has important effects on the critical crack tip opening displacement (CTOD). This value is the relevant parameter for the safe servicing of energy components (penstocks). In the case of specimens with a through thickness notch partly in the weld metal, partly in the heat affected zone and partly in the base material, i.e. using the composite notched specimen, the fracture behaviour strongly depends on the portion of ductile base material, its size and the distribution of the mismatching factor along the vicinity of the crack front. Prisotnost različnih mikrostruktur vzdolž fronte utrujenostne razpoke vpliva na kritično odpiranje konice razpoke (CTOD). Ta vrednost je relevantni parameter za varno obratovanje energetskih component (npr. zapornic hidroelektrarn). V primeru, ko je fronta konice razpoke nameščena po celotni debelini preizkušanca t.i. kompozitna razpoka in je delno prisotna v materialu zvara, toplotno vplivanem področju in osnovnem materialu, takrat je lomno obnašanje materiala odvisno od deleža žilavega osnovnega materiala, velikosti in porazdelitve faktorja trdnostne neenakosti vzdolž fronte konice razpoke. fracture toughness energy materials experimental testing energetske komponente zvarni spoji lomna žilavost true false false Angleški jezik Slovenski jezik Delo ni kategorizirano 2015-07-10 12:32:35 2015-07-10 12:32:35 2022-05-28 03:07:34 2019-07-10 21:38:27 2012 0 0 str. 39-45 iss. 3 Vol. 5 aug. 2012 0000-00-00 NiDoloceno NiDoloceno NiDoloceno 0000-00-00 0000-00-00 0000-00-00 621.791:620.1 243311360 1024110684 1855-5748 URN:SI:UM:DK:ELBQC9PK http://www.fe.uni-mb.si/images/stories/jet/e-jet/revija_jet_-_volume_5_-_issue_3_-_avgust_-_internet.pdf 1 https://dk.um.si/Dokument.php?lang=slv&id=74424 Fakulteta za energetiko 0 0 0