20.500.12556/DKUM-53310 Mehanizem nastajanja polimerne asimetrične porozne membrane z mokrim postopkom fazne inverzije Mechanism of the polymer asymmetric porous membrane formation by wet phase inversion Kvalitativno je predstavljen mehanizm nastajanja polimerne asimetrične porozne membrane po mokrem postopku fazne inverzije. Nastanek morfoloških značilnosti membran iz celuloznega acetata, polisulfona, polimetilmetakrilata,termoplastičnega poliuretana in poliamida 4,6 je interpretiran s `potmi sestave` v ternarnem faznem diagramu polimer/topilo:netopilo ter podprt z evidencami pojavov motnosti med nastajanjem membrane, skrčitve ulite raztopine polimera v (proto)membrano in s permeabilnostjo nastalih membran z vodo. The mechanism of polymeric asymmetric porous membranes prepared by the wet phase inversion process is qualitatively presented. The formation of the morphological characteristic features of membranes from cellulose acetate, polysulfone, poly(methylmetacrylate), thermoplasric polyuretane and polyamide 4,6 is interpreted in terms of the `composition path` in the ternary phase diagram polymer/solvent:nonsolvent and supported by evidences of turbidity phenomena taking place during membrane formation, shrinkage of the cast solution of polymer to the (proto)membrane, and water permeability of membranes. kemija polimeri membrane nastanek membran morfologija motnost skrčitev pretok chemistry polymers membranes membrane formation morphology turbidity shrinkage permeability true false false Inštitut za kovinske materiale in tehnologije Slovenski jezik Angleški jezik Delo ni kategorizirano 2015-07-10 20:01:36 2015-07-10 20:01:36 2022-06-03 03:09:22 2019-07-11 08:06:55 1997 0 0 str. 73-76 št. 1/2 Letn. 31 1997 0000-00-00 NiDoloceno NiDoloceno NiDoloceno 0000-00-00 0000-00-00 0000-00-00 678.7 31742209 2980886 1318-0010 URN:SI:UM:DK:NPQAR8RY http://www.dlib.si/details/URN:NBN:SI:doc-M8MLYT25 1 https://dk.um.si/Dokument.php?lang=slv&id=77870 Fakulteta za kemijo in kemijsko tehnologijo 0 0 0