20.500.12556/DKUM-56003 Comparison of NiTi orthodontic archwires and a determination of the charasteristic properties Primerjava ortodontskih lokastih žic NiTi in določitev značilnih lastnosti The aim of this paper was to analyse the characteristic properties of six different, commercially available nickel-titaniumorthodontic wires with a diameter of 0.305 mm (0.014"). The characteristic properties were determined by usingsemi-quantitative EDX analyses, DSC analyses for a determination of the phase temperatures, and a tensile test to obtain themechanical properties of the wires. The investigation of the chemical composition showed an equiatomic NiTi alloy. Analysesof phase temperatures showed that the nickel-titanium orthodontic wires were, in an austenitic microstructure, exhibiting asuperelastic effect in the oral environment. The uniaxial tensile stressstrain curves showed different values for the beginningand the end of the transformation range during the loading. Prispevek obravnava analizo karakterističnih lastnosti 6 komercialno dostopnih nikelj titanovih ortodontskih žic, ki imajo premer 0,305 mm (0,014") v fazi pred njihovo uporabo v ustih. V teh okvirih so bile analizirane mehanske lastnosti z enoosnim nateznim preizkusom, za določitev faznih temperatur pa je bila izvedena DSC-analiza ter semikvantitativna EDX-analiza. Dobljene enoosne krivulje napetost raztezek so pokazale različne vrednosti začetka in konca transformacijskega območja pri obremenjevanju NiTi-žic. Analiza faznih temperatur je potrdila, da imajo ortodontske žice avstenitno mikrostrukturo, s čimer kažejo superelastični efekt, potem ko so v uporabi v ustnem okolju. Krivulja napetost-raztezek pri enoosnem nategu je pokazala različne vrednosti za začetek in konec transformacijskega območja med obremenjevanjem. shape-memory alloy phase transformation thermal analysis tensile test nikljeve zlitine titanove zlitine zlitina s spominom oblike fazna transformacija termična analiza natezni preizkus true false true Inštitut za kovinske materiale in tehnologije Ljubljana Angleški jezik Slovenski jezik Znanstveno delo 2015-12-21 16:13:03 2015-12-21 16:13:03 2022-06-10 03:09:22 2021-05-15 03:26:13 2014 0 0 str. 99-104 št. 1 Letn. 48 jan.-feb. 2014 0000-00-00 Zaloznikova Objavljeno NiDoloceno 0000-00-00 0000-00-00 0000-00-00 1580-2949 669.245´295:620.1/.2 106193664 17585174 1580-2949 URN:SI:UM:DK:8XXGTRWB Materiali_in_Tehnologije_2014_Fercec_et_al._COMPARISON_OF_NiTi_ORTHODONTIC_ARCHWIRES_AND_A_DETERMINATION_OF_THE_CHARACTERISTIC_PROPERTIE.pdf Materiali_in_Tehnologije_2014_Fercec_et_al._COMPARISON_OF_NiTi_ORTHODONTIC_ARCHWIRES_AND_A_DETERMINATION_OF_THE_CHARACTERISTIC_PROPERTIE.pdf 1 EB6440AE3619BDEEC956DB4C605A9C4D 7d76f3fc7d66554bf5f06e05a88af3a3a2863db365c290d7077b2cbe03f903d7 fc928572-7c0d-11eb-bb7a-00155d0001ca https://dk.um.si/Dokument.php?lang=slv&id=109805 http://mit.imt.si/Revija/izvodi/mit141/fercec.pdf 1 https://dk.um.si/Dokument.php?lang=slv&id=109806 Fakulteta za strojništvo 0 0 0