20.500.12556/DKUM-65243 Synthesis of NiTi/Ni-TiO[sub]2 composite nanoparticles via ultrasonic spray pyrolysis Sinteza kompozitnih nanodelcev NiTi/Ni-TiO[sub]2 z ultrazvočno razpršilno pirolizo In this paper we present the production of NiTi/Ni-TiO2 composite nanoparticles via the synthesis method called ultrasonic spray pyrolysis (USP). The precursor solution for the synthesis of spherical NiTi particles was prepared from an orthodontic wire with a chemical composition of Ni (amount fraction x = 51.46 %) and Ti (x = 48.54 %). TEM microscopy, in combination with EDX analyses, was used for a detailed characterization of the obtained NiTi nanoparticles. The results showed the nanoparticle sizes ranging from 60 nm to 600 nm, depending on the parameters of the production procedure. This showed the versatility of the new USP synthesis procedure, proving its usefulness for different materials and applications. V tem prispevku je predstavljena izdelava NiTi/Ni-TiO2 kompozitnih nanodelcev po metodi ultrazvočne razpršilne pirolize (USP). Sferični nanodelci NiTi so bili izdelani iz ortodontske žice s kemijsko sestavo Ni (množinski delež x = 51,46 %) in Ti (x = 48,54 %). Za karakterizacijo nanodelcev je bila uporabljena TEM-mikroskopija v kombinaciji z EDX-analizo. Rezultati meritev so pokazali velikostno porazdelitev narejenih nanodelcev v razponu od 60 nm do 600 nm v odvisnosti od parametrov izdelave. To potrjuje vsestranskost novega izdelovalnega postopka USP in njegovo uporabnost za različne materiale in aplikacije. ultrasonic spray pyrolysis NiTi/Ni-TiO2 composite nanoparticles characterization Transmission electron microscope (TEM) TEM microscopy ultrazvočna razpršilna piroliza NiTi/Ni-TiO2 kompozitni nanodelci karakterizacija TEM mikroskopija true false true Angleški jezik Slovenski jezik Znanstveno delo 2017-03-23 15:31:50 2017-03-23 15:33:17 2022-07-07 03:08:52 2019-07-11 15:12:08 2015 0 0 str. 75-80 št. 1 Letn. 49 2015 0000-00-00 Zaloznikova Objavljeno NiDoloceno 0000-00-00 0000-00-00 0000-00-00 1580-2949 620.3:669.018.9.017 106193664 18403094 1580-2949 URN:SI:UM:DK:HF0NKMCS Materiali_in_tehnologije_2015_Majeric_et_al._Synthesis_of_NiTiNi-TiOsub2_composite_nanoparticles_via_ultrasonic_spray_pyrolysis.pdf Materiali_in_tehnologije_2015_Majeric_et_al._Synthesis_of_NiTiNi-TiOsub2_composite_nanoparticles_via_ultrasonic_spray_pyrolysis.pdf 1 A4D8C91C44E552A54641E7BDDA62A313 cd11b3d087de27276b75fdf38683ba6bcd72d6c889803cd3dc3f250943465137 03483216-7c0e-11eb-bb7a-00155d0001ca https://dk.um.si/Dokument.php?lang=slv&id=110090 http://mit.imt.si/Revija/izvodi/mit151/majeric.pdf 1 https://dk.um.si/Dokument.php?lang=slv&id=110089 Fakulteta za strojništvo 0 0 0