20.500.12556/DKUM-66571 Fatigue crack growth and fracture mechanics analysis of a working roll surface layer material Fatigue crack growth and fracture mechanics analysis of a working roll surface layer material is presented in this paper. The research is done on a hot strip mill working roll where High Chromium Steel is used for roll’s shell material. To obtain corresponding parameters, a rectangular single edge notched bend specimens – SENB, according to standard BS 7448, were used. The fatigue crack growth analysis was done on a resonant testing machine with use of special crack gauges, while for fracture mechanics parameters the electro–mechanical testing machine was used. fracture mechanics fatigue crack growth metal forming rolling process high chromium steel mehanika loma rast razpoke rast utrujenostne razpoke utrujenost materiala visoko legirano kromovo jeklo preiskava materiala true false true Angleški jezik Slovenski jezik Znanstveno delo 2017-07-03 13:14:36 2017-07-03 13:15:32 2022-08-01 12:55:41 2019-07-11 15:51:52 2014 0 0 str. 481-484 št. 4 Letn. 53 2014 0000-00-00 Zaloznikova Objavljeno NiDoloceno 0000-00-00 0000-00-00 0000-00-00 1334-2576 539.42:621.77 6892802 17828886 1334-2576 URN:SI:UM:DK:QA76CDNU Metalurgija_2014_Drobne_et_al._Fatigue_Crack_Growth_and_Fracture_Mechanics_Analysis_of_a_Working_Roll_Surface_Layer_Material.pdf Metalurgija_2014_Drobne_et_al._Fatigue_Crack_Growth_and_Fracture_Mechanics_Analysis_of_a_Working_Roll_Surface_Layer_Material.pdf 1 594D5F3D19E78349853473F4690E2E90 f6e5d988ddf7cba3b3a564a683e07827ee2e367c64d8914c2d0abb6eefe973b4 5684bdff-7c0e-11eb-bb7a-00155d0001ca 20.500.12556/dkum/a566a1e3-f62c-4597-83fe-a151e12ffe74 https://dk.um.si/Dokument.php?lang=slv&id=113488 http://hrcak.srce.hr/122168 1 https://dk.um.si/Dokument.php?lang=slv&id=113487 Fakulteta za strojništvo 0 0 0