20.500.12556/DKUM-66804 Compression pre-stress of tubular torsion springs Tlačno prednaprezanje cjevastih torzijskih opruga This paper reports the results of a series of biaxial static compression and torsion experiments performed to evaluate the effects of static compression stress on the fatigue life of those smooth tubes made of high strength spring steel. The fatigue life of biaxial loaded springs depends, among others, on biaxial compression and torsion loading. A high shear loading ratio leads to low-cycle fatigue behaviour rather than high-cycle fatigue, because it was found that a crack was initiated at a local highly deformed area on surface of the specimen.The experimentally obtained results show a significant extension of fatigue strain life as a result of combining axial compression loading with torsion. Cracking behaviour was observed and it was noted that compression pre-stresses contribute to retardation of the fatigue crack initiation process and, consequently, contribute to the extension of fatigue life. U ovom se radu iznose rezultati niza eksperimenata dvoosnog statičkog tlačnog i torzijskog opterećenja kako bi se procijenilo djelovanje omjera tlačne napetosti na zamorni vijek trajanja cijevi napravljenih od visoko čvrstog čelika za opruge.Vijek trajanja dvoosno opterećenih opruga obzirom na zamor ovisi, između ostaloga, o biaksijalnom tlačnom i torzijskom opterećenju. Omjer opterećenja kod visokog smičnog naprezanja dovodi do nisko cikličkog više nego visoko cikličkog zamora jer se ustanovilo da se pukotina pojavila na lokalnom krajnje deformiranom dijelu na površini uzorka. Eksperimentalno dobiveni rezultati pokazuju značajan produžetak vijeka trajanja deformacije zbog zamora kao rezultat kombiniranja aksijalnog tlačnog i torzijskog opterećenja. Primijećena je pojava pukotina i zapaženo da tlačna prednaprezanja dovode do usporavanja procesa nastajanja zamornih pukotina i stoga doprinose produženju vijeka trajanja obzirom nazamor. fatigue fatigue life micro crack multi axial stress state pre-stressing torsion torsion bar springs twist angle utrujenost mikro razpoke večaksialno stanje napetosti prednapenjanje torzija torzijske vzmeti kot zvijanja true false true Angleški jezik Hrvaški jezik Znanstveno delo 2017-07-11 12:04:12 2017-07-11 12:04:56 2022-08-01 13:11:22 2019-07-11 15:59:29 2010 0 0 str. 307-315 št. 3 Letn. 17 2010 0000-00-00 Zaloznikova Objavljeno NiDoloceno 0000-00-00 0000-00-00 0000-00-00 1330-3651 539.3:620.175.22 15346181 14522134 1330-3651 URN:SI:UM:DK:FAWZGDZS Tehnicki_vjesnik_2010_Mocilnik_et_al._Compression_pre-stress_of_tubular_torsion_springs.pdf Tehnicki_vjesnik_2010_Mocilnik_et_al._Compression_pre-stress_of_tubular_torsion_springs.pdf 1 2C949E1E6E25AF21B0996E324095CF67 6e3d39f63df57ec9504306b91f4968e3b98c2fff11b07241b0781a6d736a6e0a 6525e3d0-7c0e-11eb-bb7a-00155d0001ca 20.500.12556/dkum/f6eacad6-0283-4add-98c2-83f2e4281a45 https://dk.um.si/Dokument.php?lang=slv&id=114012 http://hrcak.srce.hr/59643 1 https://dk.um.si/Dokument.php?lang=slv&id=114011 Fakulteta za strojništvo 0 0 0