20.500.12556/DKUM-83476 Proučevanje vpliva silažne folije na okolje magistrsko delo Study on the impact of silage foil on the environment Vsesplošna rast rabe plastičnih materialov je vidna na vseh področjih, tudi na področju kmetijstva, kjer ima nekatere pozitivne učinke. Pozitivne lastnosti plastičnih materialov v času rabe postanejo okoljsko breme po koncu uporabe, ko je material treba odstraniti. V raziskovalnem delu smo opazovali in okarakterizirali degradacijo folije iz polietilena nizke gostote (LDPE), ki se uporablja za zaščito silaže in bal za seno. Oceno degradacije materiala zaradi izpostavljenosti okoljskim vplivom smo izvedli z laboratorijskimi simulacijami teh pogojev v vodnem mediju, v zemlji in s pomočjo komore za simulacijo vremenskih vplivov (ksenon test). Za karakterizacijo materiala smo uporabili infrardečo spektroskopijo s Fourierjevo transformacijo, termogravimetrično analizo, goniometrijo, gravimetrijo, optično mikroskopijo, karakterizacijo sežiga materiala in analizo vodnega medija. Glavne ugotovitve karakterizacije LDPE folije so, da na degradacijo najbolj vpliva ultravijolično sevanje, vendar je material obdelan tako, da v kratkem času izpostavljenosti vremenskim vplivom ne pride do drastičnih sprememb lastnosti. Zaradi tega je pomembno kaj se z materialom zgodi po uporabi, ko ga zavržemo. The widespread growth in the use of plastic materials is visible in all areas, including agriculture, where it is having some positive effects. Positive properties of plastic materials at the time of use become an environmental burden when being disposed of. In this research, the degradation of low-density polyethylene (LDPE) film wrap used to protect silage and hay bales was observed and characterized. The assessment of the degradation of the material due to exposure to environmental impacts was carried out by laboratory simulations of these conditions in aqueous media, in soil, and with weathering simulation chamber (xenon test). Fourier-transformed infrared spectroscopy, thermogravimetric analysis, goniometry, gravimetry, optical microscopy, characterization of the burning of the material, and analysis of the aqueous media were used to characterize the material. The main findings from the characterization of the LDPE film are that degradation is most affected by ultraviolet (UV) radiation, but the material is treated in such a way that no drastic changes in properties occur in a short exposure time to weathering. It is therefore important what happens to the material after use when it is disposed of. silažna folija polietilen nizke gostote (LDPE) degradacija ksenon test izpostavljenost v zemlji izpostavljenost v vodi. silage foil low-density polyethylene (LDPE) degradation xenon test soil burial test exposure in water true true false [N. Lebar] Slovenski jezik Angleški jezik Magistrsko delo/naloga 2022-12-02 11:57:10 2023-01-05 12:54:03 2023-05-12 03:06:42 0000-00-00 00:00:00 2022 0 Maribor 0 Maribor 1 spletni vir (1 datoteka PDF (XIV, 68 f.)) 0000-00-00 NiDoloceno NiDoloceno NiDoloceno 0000-00-00 0000-00-00 0000-00-00 [504.5:678.742.2]:631(043.2) 151769859 MAG_Lebar_Nejc_2023.pdf MAG_Lebar_Nejc_2023.pdf 1 E320E2BBB4D4AA34185398992E29F742 1f541a076b2cabdb36240db6f0030f6dccad705de5fc05307886cce1dbe78660 b7d8e8d1-8cd2-11ed-a651-00155d000105 https://dk.um.si/Dokument.php?lang=slv&id=165061 Fakulteta za strojništvo 0 0 0