20.500.12556/DKUM-86628 Fracture toughness of HSLA welds made on penstock material Lomna žilavost HSLA zvarov zgrajenih na jeklih za vodne zapornice The presence of different microstructures along the pre-crack fatigue front has a significant effect on the critical crack tip opening displacement (CTOD). This value is the relevant parameter for the safe servicing of welded structures (penstocks). In the case of specimens with the through-thickness notch partly in the weld metal, partly in the heat-affected zone, and partly in the base material, i.e., using the composite notched specimen, the fracture behaviour significantly depends on the portion of the ductile base material, the size, and the distribution of mismatching factor along the vicinity of the crack front. Prisotnost različnih mikrostruktur na fronti konice utrujenostne razpoke ima pomemben vpliv na odpiranje konice razpoke (CTOD). Ta vrednost je relevantni parameter za varno obratovanje varjenih konstrukcij (vodne zapornice). V primeru preizkušancev z globoko razpoko, kjer fronta konice razpoke zajema del zvara, toplotno vplivanega področja in osnovnega materiala, t.i. kompozitno razpoko v preizkušancih, je lomno obnašanje odvisno od deleža žilavega osnovnega materiala, ter velikosti in porazdelitve faktorja trdnostne neenakosti vzdolž fronte razpoke. High Strength low Alloyed Steel CTOD Fracture Toughness Testing CTOD-R resistance Curve Welded joints jeklo z visoko trdnostjo nizko legirano jeklo CTOD testiranje preizkus pomika odpiranja konice razpok CTOD-R krivulje varjeni spoji true false true Fakulteta za energetiko Univerze v Mariboru Angleški jezik Slovenski jezik Znanstveno delo 2023-12-22 11:20:29 2023-12-22 11:36:53 2023-12-23 03:38:09 0000-00-00 00:00:00 2019 0 0 Str. 51-60 Št. 4 Letn. 12 dec. 2019 0000-00-00 Zaloznikova Objavljeno NiDoloceno 0000-00-00 0000-00-00 2019-12-01 621.791.053:620.179.2 1024386396 1855-5748 Fracture-toughness_of_HSLA_welds_Praunseis_2019.pdf Fracture-toughness_of_HSLA_welds_Praunseis_2019.pdf 1 DC46D9495BF9F48E9F0D25DEE40805B7 c79fbf0534ae2393b7f8391dc726435263d3e9a522d237ab8b9dc9d722266b54 f4069564-a0b5-11ee-9a5d-00155d000105 https://dk.um.si/Dokument.php?lang=slv&id=175018 https://www.fe.um.si/e-jet/38-2019/2060-december-2019.html 0 fe1f03da-a0b5-11ee-9a5d-00155d000105 https://dk.um.si/Dokument.php?lang=slv&id=175019 Fakulteta za energetiko Journal of energy technology 0 0 0