20.500.12556/DKUM-91271 Corrosion characterization and ion release in SLM-manufactured and wrought Ti6Al4V alloy in an oral environment As-produced and heat-treated TiAlV samples were prepared by selective laser melting and compared to wrought samples of identical chemical composition. Microstructural, corrosion, and spectroscopic studies of additively manufactured samples in artificial saliva at 37 °C, with NaF and at pH 2.3 were as a novelty combined with metal ion release during 42 days immersion. In artificial saliva higher amount of ions was released on SLM specimen when compared to wrought alloy. The total amount of ions released from SLM specimen in AS containing NaF was 10-times higher than in AS, while in AS with lactic acid it was 100-times higher. Ti6Al4V SLM corrosion ion release XPS ToF-SIMS Ti6Al4V SLM korozija sproščanje ionov XPS ToF SIMS true false true Pergamon Press Angleški jezik Slovenski jezik Znanstveno delo 2024-12-05 14:20:01 2024-12-05 14:35:50 2024-12-06 03:20:53 0000-00-00 00:00:00 2022 0 0 Str. 1-15 št. članka 110716 Letn. 209 2022 0000-00-00 Zaloznikova Objavljeno NiDoloceno 2022-06-23 2022-10-01 2022-10-04 544.5/.6 124149507 10.1016/j.corsci.2022.110716 0010-938X Leban_2022_Corrosion_characterization.pdf Leban_2022_Corrosion_characterization.pdf 1 F76F17A0CE73589035160D29548CD8B8 8665c1c3794128e116ee8988dcd3a43a62a5cea4a7a327fa0809fe0a2301480d 6d56302b-b30d-11ef-9aff-00155d000105 https://dk.um.si/Dokument.php?lang=slv&id=187144 https://doi.org/10.1016/j.corsci.2022.110716 0 a288bb9f-b30b-11ef-9aff-00155d000105 https://dk.um.si/Dokument.php?lang=slv&id=187143 Fakulteta za kemijo in kemijsko tehnologijo 0 0 0