20.500.12556/DKUM-94331 Magnetna rastlinska nanoceluloza za učinkovito odstranjevanje onesnaževal diplomsko delo visokošolskega strokovnega študijskega programa I. stopnje Magnetic nanocellulose for efficient pollutant removal Onesnaževanje okolja z težkimi kovinami predstavlja vse večji globalni problem, saj se z naraščajočo industrializacije in urbanizacije njihova koncentracija v okolju povečuje. Zaradi njihove visoke toksičnosti v že zelo majhnih koncentracijah imajo negativne vplive na ljudi in okolje. Med različnimi metodami je se adsorpcija izkazala kot ena izmed najučinkovitejših, najpreprostejših in cenovno ugodnih tehnik. Kot absorbent se vse pogosteje uporabljajo biorazgradljivi polimeri, saj predstavljajo okolju prijazno in trajnostno alternativo v primerjavi z tradicionalnimi adsorbenti. V diplomskem delu smo se osredotočali predvsem na magnetno nanocelulozo, kot adsorbent za odstranjevanje kromovih ionov raztopine Kr2Cr2O7. Cilj diplomske naloge je bil izolirati nanocelulozni material iz praproti Polypodiophyta. Uspešno sintetizirali magnetno nanocelulozo s pomočjo železovih Fe(II) in Fe(III) ionov. Pripravljeni materialsmo nato uporabili pri odstranjevnaju kromovih ionov katero smo v nadaljevanju uporabili za odstranjevanje Cr(VI) ionov iz vodne raztopine. Določevali smo optimalne pogoje za največjo učinkovitost adsorpcije kromovih ionov, pri čemer smo se osredotočali na pH raztopine, koncentracijo kromovih ionov v vodni raztopini. Morfološke značilnosti adsorbenta pred in po adsorpciji smo analizirali z SEM analizo, TGA/DSC analizo in FTIR spektroskopijo. Za opis mehanizma adsorpcijskih procesov pa smo uporabili Freundlichovo in Langmuierjevo metodo. Rezultati so pokazali, da se kromovi ioni najboljše adsorbirajo v kislem mediju, saj je bil največji učinek adsorpcije dosežen pri pH v vrednosti 5, saj je dosegel kar 98,84 % učinkovitost adsorpcije. Določevanje vpliva masne koncentracije medija, smo prišli do ugotovitev, da večje število prostih mest na površini adsorbenta omogoča hitrejšo adsorpcijo kromovih ionov. V našem primeru je največji učinek adsorpcije dosegel pri koncentraciji 1,00 g/mL. Environmental pollution whith heavy metals represents an increasing global problem as their concentration in the environment continous to rise due to growing inndustrialization and urbanization. Because of theit high toxicity, even at very low concentration, heavy metals have adverse effect on both human health and the environment. Among the various methods, adsorption has proven to be one of the most effective, simplest, and most cost-efficient techniques.In recant years, biodegradable polymers have been increasingly used as adsorbents, as they represent an anvironmentally friendly and sustainable alternative to traditional adsorbents. In this thesis was to isolate nanocellulosic material from ferns (Polypodiophyta). Magnetic nanocellulose was successfully synthesised using Fe(II) and Fe(III) ions. The prepared material was than applied for removal of chromium ions from aqueous solution. We determined the optimal conditions for maximum adsorption efficiency of chromium ions, focusing on the pH of the solution and the concentration of chromium ions in the aqueous medium. The morphological characteristics of the adsorbent before and after adsorption were analyzed using SEM, TGA/DSC analysis, and FTIR spectroscopy. To describe the mechanism of the adsorption process, Freundlich and Langmuir methodst were also applied. The results showed thta Cr(VI) was more effectively adsorbed in an acidic medium, whith the highest adsorption efficiency (98,84%) achieved at pH 5, in the experiments investigating the effect of mass concentration, it was observed that a greater number of available active sites on the adsorbent surface enable faster adsorption of chromium ions. In our case, the highest adsorption efficiency was obtained at a magnetic nanocellulose concentration of 1,00 g/mL. magnetna nanoceluloza krom adsorpcija težke kovine magnetic nanocellulose chromium adsorption heavy metals true true false [T. Gajić] Slovenski jezik Angleški jezik Diplomsko delo/naloga 2025-08-13 16:09:06 2025-09-23 13:05:38 2025-10-30 03:15:15 0000-00-00 00:00:00 2025 0 Maribor 0 Maribor 1 spletni vir (1 datoteka PDF (X, 37 str.)) 0000-00-00 NiDoloceno NiDoloceno NiDoloceno 0000-00-00 0000-00-00 0000-00-00 547.458.8:[66..081.3:546.76](043.2) 255281923 VS_Gajic_Tajda_2025.pdf VS_Gajic_Tajda_2025.pdf 1 607F8748861C30E0C0541842E12B074A b14a157b87857128b9e96d3f542105e23f1ae06c6ab916c0410539be5d3a12da 6ee85009-9303-11f0-8742-00155d000105 https://dk.um.si/Dokument.php?lang=slv&id=198600 Fakulteta za kemijo in kemijsko tehnologijo 0 0 0