20.500.12556/DKUM-95863 Mechanical uniaxial compression of 3D-printed non-periodic ASA lattice structures using semi-controlled design models This work examines the mechanical behaviour of 3D-printed stochastic lattice structures fabricated using a semi-controlled design. A primary goal is to predict and optimize the mechanical response of these Acrylic Styrene Acrylonitrile (ASA) filament structures when subjected to compressive stress. By transitioning from a purely stochastic method to a semi-controlled tessellation approach within Rhinoceros 7 software, we effectively generated the proposed design models. This methodology results in mechanical responses that are both predictable and reliable. The design parameters, including nodal formation, strut thickness, and lattice generation based on a predefined geometric routine, are associated with the regulation of the relative density. This approach aims to minimize the effect of relative density on the actual stiffness and strength evaluation. Our findings are cantered on the compressive testing of structures, which were generated using a Voronoi population distributed along a parabolic curve. We analyzed their mechanical response to the point of failure by examining stress–strain fluctuations. Three distinct behaviour stages are observed: elastic range, plastic range, and collapse without densification. The influence of crosslink geometry on the elastic responses was highlighted, with parabolic configurations affecting the peak stresses and elastic line slopes. The structures exhibited purely brittle behaviour, characterized by abrupt local cracking and oscillatory plateau formation in the plastic stage. semi-controlled Voronoi tessellation stress–strain curve mechanical response delno nadzorovana Voronojeva teselacija krivulja napetosti in deformacije mehanski odziv true false true MDPI Angleški jezik Slovenski jezik https://www.mdpi.com/2073-4360/17/20/2775 Članek v reviji 2025-11-03 11:56:05 2025-11-03 11:56:06 2025-11-04 03:34:50 0000-00-00 00:00:00 2025 0 0 20 str. no. 20, [article no.] 2775 vol. 17 October 2025 0000-00-00 Zaloznikova Objavljeno NiDoloceno 2025-09-09 2025-10-13 2025-10-16 62‑965 66642438 10.3390/polym17202775 2073-4360 polymers-17-02775-v2_(1).pdf polymers-17-02775-v2_(1).pdf 1 84A1A1CE783E768712458D479CEE5B8D 9f39f08e46811fa8d3b28d496bf35d443a13e9831dfc410da67d92dea2dc7050 31cc75ea-b8a4-11f0-b13b-00155d000105 https://dk.um.si/Dokument.php?lang=slv&id=200339 https://www.mdpi.com/2073-4360/17/20/2775 0 5bdceed3-b8a4-11f0-b13b-00155d000105 https://dk.um.si/Dokument.php?lang=slv&id=200340 Fakulteta za strojništvo 0 0 0