20.500.12556/DKUM-97290 Evaluation of the mechanical properties of steel under elevated temperature conditions Analiza mehanskih lastnosti jekla pri povišanih temperaturah This paper presents the influence of elevated temperatures on the mechanical properties of steel with varying iron content and alloying compositions. The paper combines chemical analysis and high-temperature tensile testing to examine how microstructure, chemical composition and temperature affect the yield strength, tensile strength and ductility of steel. Samples of two thicknesses (0.63 mm and 0.50 mm) and three iron levels (85 wt%, 90 wt %, and 97 wt%) were analysed and classified based on their chemical composition. Tensile tests were performed in accordance with ISO 6892-2 within the temperature range of 90 °C to 250 °C, using 20 °C increments. The findings highlight the combined effect of temperature and alloying chemistry on the high-temperature performance of steel, providing valuable insights for material selection in thermally demanding engineering applications. Članek predstavlja vpliv povišanih temperatur na mehanske lastnosti jekla z različno vsebnostjo železa in legirnimi dodatki. V raziskavi so združeni kemijska analiza in natezni preizkusi pri povišanih temperaturah z namenom preučitve vpliva mikrostrukture, kemijske sestave in temperature na mejo tečenja, natezno trdnost in duktilnost jekla. Analizirani in razvrščeni so bili vzorci dveh debelin (0,63 mm in 0,50 mm) ter treh vsebnosti železa (85 mas. %, 90 mas. % in 97 mas. %), glede na njihovo kemijsko sestavo. Natezni preizkusi so bili izvedeni v skladu s standardom ISO 6892-2 v temperaturnem območju od 90 °C do 250 °C, v korakih po 20 °C. Rezultati poudarjajo skupni vpliv temperature in legirne kemije na obnašanje jekla pri povišanih temperaturah ter zagotavljajo dragocene usmeritve za izbiro materialov v termično zahtevnih inženirskih aplikacijah. steel tensile test temperature chemical analysis stress-strain diagram alloying elements jeklo natezni preizkus temperatura kemijska analiza diagram napetosti in deformacije legirni elementi true false true Angleški jezik Slovenski jezik Neznano 2026-02-26 12:45:04 2026-02-26 12:45:05 2026-02-27 03:17:45 0000-00-00 00:00:00 2025 0 0 str. 231-250 Št. 4 Letn. 18 dec. 2025 0000-00-00 Zaloznikova Objavljeno NiDoloceno 2025-12-01 2025-12-18 2025-12-31 669.1 268886019 1855-5748 Evaluation_of_the_mechanical_pr-Sredensek-2025.pdf Evaluation_of_the_mechanical_pr-Sredensek-2025.pdf 1 5B51434D75F0B392C289739F0471D2E1 ba55544e7b4eaf59261f15f002bade99ee73756d58721eb1175dd43d4b06d1b5 fc681e2c-1308-11f1-94ed-00155d580e1a https://dk.um.si/Dokument.php?lang=slv&id=203946 https://journals.um.si/index.php/jet/article/view/5665/3546 0 41d5b22a-1309-11f1-94ed-00155d580e1a https://dk.um.si/Dokument.php?lang=slv&id=203947 Fakulteta za energetiko Univerzitetna založba Univerze v Mariboru Journal of energy technology 0 0 0