20.500.12556/DKUM-97393 Recikliranje plastičnih polikarbonatnih odpadkov s hidrotermičnimi postopki magistrsko delo Recycling of policarbonate plastics waste using hydrothermal Naraščajoče količine plastičnih odpadkov in omejitve mehanskega recikliranja poudarjajo potrebo po razvoju učinkovitih metod kemijskega recikliranja. V magistrskem delu smo preučevali hidrotermično razgradnjo odpadnih polikarbonatnih zgoščenk (CD-jev) v pod- in nadkritični vodi z namenom ovrednotenja vpliva temperature in reakcijskega časa na stopnjo razgradnje ter porazdelitev in sestavo produktov. Eksperimenti so potekali v temperaturnem območju od 250 do 450 °C in reakcijskih časih od 5 do 60 min. Produkte smo analizirali s termogravimetrično analizo (TGA), infrardečo spektroskopijo (FTIR), plinsko kromatografijo (GC-FID) ter analizirali celokupni ogljik (TC) v vodni fazi. Rezultati so pokazali, da je temperatura ključni parameter procesa: pri 250 °C je ostalo 77,0 % nedegradiranega materiala, pri 300 °C je že prišlo do izrazite razgradnje, medtem ko je bil pri temperaturah 400 in 450 °C dosežen tudi do 96,9 % izkoristek organske faze. Največji delež bisfenola A (28,5 %) je bil dosežen pri 250 °C in 60 min, medtem ko sta se pri višjih temperaturah povečevala deleža fenola (do 36,7 %) in 4-izopropilfenola (do 20,8 %), ob hkratnem povečanju deleža plinske faze do 9,0 %. Ugotovitve potrjujejo, da je s prilagajanjem procesnih pogojev mogoče usmerjati selektivnost reakcije, pri čemer hidrotermična obdelava predstavlja učinkovito in perspektivno metodo kemičnega recikliranja polikarbonatnih odpadkov v okviru trajnostnih pristopov krožnega gospodarstva. The increasing volume of plastic waste and the limitations of mechanical recycling underscore the need to develop effective chemical recycling methods. In this master's thesis, the hydrothermal degradation of waste polycarbonate compact discs (CDs) in subcritical and supercritical water was investigated, aiming to evaluate the influence of temperature and reaction time on the degree of degradation and product distribution. Experiments were conducted at temperatures ranging from 250 to 450 °C and reaction times from 5 to 60 minutes. The products were analysed by thermogravimetric analysis (TGA), infrared spectroscopy (FTIR), gas chromatography (GC-FID), and analysis of total carbon (TC) content. The results showed that temperature is a key parameter in the process: at 250 °C, 77.0% of the solid phase remained undegraded, while at 300 °C the degree of degradation increased significantly, and at 400 and 450 °C up to 96.9% of the organic phase was recovered. The highest proportion of bisphenol A (28.5%) was achieved at 250 °C and 60 minutes, while at higher temperatures the proportions of phenol (up to 36.7%) and 4-isopropylphenol (up to 20.8%) increased, with a simultaneous increase in the gas phase to 9.0%. These findings confirm that the selectivity of the reaction can be controlled by adjusting the process conditions, with hydrothermal treatment representing an effective and promising method for the chemical recycling of polycarbonate waste within the framework of sustainable circular economy approaches. polikarbonat hidrotermična razgradnja nadkritična voda plastični odpadki bisfenol A polycarbonate hydrothermal degradation supercritical water plastic waste bisphenol A true true false [K. Kogovšek] Slovenski jezik Angleški jezik Magistrsko delo/naloga 2026-03-03 12:35:11 2026-05-04 10:32:54 2026-05-07 03:10:24 0000-00-00 00:00:00 2026 0 Maribor 0 Maribor 1 spletni vir (1 datoteka PDF (X, 51 str.)) 0000-00-00 NiDoloceno NiDoloceno NiDoloceno 0000-00-00 0000-00-00 0000-00-00 [66.092:54-139]: 547.56(043.2) 277155587 MAG_Kogovsek_Kristjan_2026.pdf MAG_Kogovsek_Kristjan_2026.pdf 1 338C11F6BE28D0AB8C158E60719F5D55 424f471cd9ed541f93db57345b985739c0d748ef27cbb20e2d5953de3c75c049 5027269e-4265-11f1-a991-00155d0001a1 https://dk.um.si/Dokument.php?lang=slv&id=205657 Fakulteta za kemijo in kemijsko tehnologijo 0 0 0