20.500.12556/DKUM-97463 Quasi‐static and fatigue strength of copper‐brazed  stainless steel  This study investigates the quasi‐static and fatigue strength of copper‐brazed 316L stainless steel. Quasi‐static and fatigue tests were conducted at room temperature (20 °C) using a Zwick/Roell Vibrophore 100 testing machine and specially designed copper‐brazed specimens. Two types of specimens were prepared—tensile and shear specimens—to obtain the stress–strain relationships (σ–ε and τ–ε) and the fatigue life (S–N) curves. Based on the experimental results, the quasi‐static and fatigue strengths of the copper‐brazed joints under external tensile and shear loading were evaluated. The fatigue tests reveal that the shear fatigue strength is significantly lower than the tensile fatigue strength. Furthermore, a comprehensive investigation was conducted, focusing on the metallographic characterisation of the brazed joint and fractographic analyses of fracture surfaces obtained under quasi‐static and fatigue loading, with particular emphasis on the shear strength of the investigated brazed joint. The experimental results obtained may be crucial for designing engineering structures (e.g., plate heat exchangers), where copper‐brazed joints are the weakest members of the structure.  copper‐brazed joint quasi‐static testing fatigue testing metallographic investigation  bakreno spajkani spoj kvazistatično testiranje testiranje utrujanja metalografske preiskave true false true MDPI Angleški jezik Slovenski jezik https://www.mdpi.com/2076-3417/16/4/2160 Članek v reviji 2026-03-10 15:20:38 2026-03-10 15:20:38 2026-03-11 03:07:58 0000-00-00 00:00:00 2026 0 0 17 str. iss. 4, [article no.] 2160 Vol. 16 Feb. 2026 0000-00-00 Zaloznikova Objavljeno NiDoloceno 2026-01-20 2026-02-20 2026-02-23 621.791:620.1 271023619 10.3390/app16042160  2076-3417 applsci-16-02160-v2.pdf applsci-16-02160-v2.pdf 1 28CC8196F5F4CE1AFC5835FF453B0375 1b533f7dfafe07b06fa5ac636ab5833cb507f1247b7408fd34f95a82ffa696b0 94bd162c-1c8c-11f1-bd80-00155d580e1a https://dk.um.si/Dokument.php?lang=slv&id=204410 https://www.mdpi.com/2076-3417/16/4/2160 0 9d109c36-1c8c-11f1-bd80-00155d580e1a https://dk.um.si/Dokument.php?lang=slv&id=204411 Fakulteta za strojništvo 0 0 0