| Naslov: | Composition and morphology of diborides in Al-Ti-B alloys after annealing at 1873 K |
|---|
| Avtorji: | ID Zupanič, Franc (Avtor) |
|---|
| Datoteke: |  http://www.rmz-mg.com/letniki/rmz55/RMZ55_1.pdf
|
|---|
| Jezik: | Angleški jezik |
|---|
| Vrsta gradiva: | Neznano |
|---|
| Tipologija: | 1.01 - Izvirni znanstveni članek |
|---|
| Organizacija: | FS - Fakulteta za strojništvo
|
|---|
| Opis: | In the investigation, Al-Ti-B alloys with different Ti/B ratios were annealed at 1873 K for 10 hours. Under this condition diboride particles were in contact with molten aluminium. During annealing considerable growth of remaining unmelted diboride particles took place. The composition of diboride particles shifted extremely close to the composition of pure TiB2 regardless of the Ti/B ratios in the alloys, indicating that in equilibrium almost pure TiB2 coexisted with a melt. Diboride particles were bound with well-defined crystal facets. Types and relative size of the facets depended on the Ti/B ratio. It is strongly indicated that an excess of Ti (B) in the melt over that needed to form TiB2 stabilizes crystal planes having planar arrangement of Ti (B) atoms.V tej raziskavi smo več zlitin Al-Ti-B, ki so imele različna razmerja Ti/B, žarili 10 ur pri 1873 K. V teh razmerah so bili delci diborida v kontaktu z aluminijevo talino. Med žarjenjem so diboridni delci močno zrasli. Njihova sestava se je v vseh raziskanih zlitinah močno približala sestavi čistega TiB2, kar kaže, da je v termodinamskem ravnotežju s talino praktično čisti TiB2. Diboridni delci so bili obdani s kristalnimi fasetami. Vrsta in relativna velikost faset je bila močno odvisna od razmerja Ti/B. Obstajajo trdni dokazi, da presežek Ti (B) nad vrednostjo, ki je potrebna za tvorbo TiB2, stabilizira kristalne ravnine, ki imajo ravninsko razporeditev Ti (B) atomov. |
|---|
| Ključne besede: | Al-Ti-B alloys, diboride phase, high-temperature annealing, morphology, microstructure |
|---|
| Leto izida: | 2008 |
|---|
| PID: | 20.500.12556/DKUM-26153  |
|---|
| UDK: | 669 |
|---|
| COBISS.SI-ID: | 12150806 |
|---|
| ISSN pri članku: | 1408-7073 |
|---|
| NUK URN: | URN:SI:UM:DK:6CATSSGU |
|---|
| Datum objave v DKUM: | 31.05.2012 |
|---|
| Število ogledov: | 2150 |
|---|
| Število prenosov: | 25 |
|---|
| Metapodatki: |    |
|---|
| Področja: | Ostalo
|
|---|
|
:
|
Kopiraj citat |
|---|
| | | | Skupna ocena: | (0 glasov) |
|---|
| Vaša ocena: | Ocenjevanje je dovoljeno samo prijavljenim uporabnikom. |
|---|
| Objavi na: |  |
|---|
Postavite miškin kazalec na naslov za izpis povzetka. Klik na naslov izpiše
podrobnosti ali sproži prenos. |