Vaš brskalnik ne omogoča JavaScript!
JavaScript je nujen za pravilno delovanje teh spletnih strani. Omogočite JavaScript ali uporabite sodobnejši brskalnik.
|
|
SLO
|
ENG
|
Piškotki in zasebnost
DKUM
EPF - Ekonomsko-poslovna fakulteta
FE - Fakulteta za energetiko
FERI - Fakulteta za elektrotehniko, računalništvo in informatiko
FF - Filozofska fakulteta
FGPA - Fakulteta za gradbeništvo, prometno inženirstvo in arhitekturo
FKBV - Fakulteta za kmetijstvo in biosistemske vede
FKKT - Fakulteta za kemijo in kemijsko tehnologijo
FL - Fakulteta za logistiko
FNM - Fakulteta za naravoslovje in matematiko
FOV - Fakulteta za organizacijske vede
FS - Fakulteta za strojništvo
FT - Fakulteta za turizem
FVV - Fakulteta za varnostne vede
FZV - Fakulteta za zdravstvene vede
MF - Medicinska fakulteta
PEF - Pedagoška fakulteta
PF - Pravna fakulteta
UKM - Univerzitetna knjižnica Maribor
UM - Univerza v Mariboru
UZUM - Univerzitetna založba Univerze v Mariboru
COBISS
Ekonomsko poslovna fakulteta
Fakulteta za kmetijstvo in biosistemske vede
Fakulteta za logistiko
Fakulteta za organizacijske vede
Fakulteta za varnostne vede
Fakulteta za zdravstvene vede
Knjižnica tehniških fakultet
Medicinska fakulteta
Miklošičeva knjižnica - FPNM
Pravna fakulteta
Univerzitetna knjižnica Maribor
Večja pisava
|
Manjša pisava
Uvodnik
Iskanje
Brskanje
Oddaja dela
Statistika
Prijava
Prva stran
>
Izpis gradiva
Izpis gradiva
Naslov:
Some factors affecting fatigue resistance of welds
Avtorji:
ID
Gliha, Vladimir
(
Avtor
)
ID
Burzić, Zijah
(
Avtor
)
ID
Vuherer, Tomaž
(
Avtor
)
Datoteke:
http://www.divk.org.rs/ivk/ivk10/239-244-IVK3-2010-VG-ZB-TV.pdf
Jezik:
Angleški jezik
Vrsta gradiva:
Neznano
Tipologija:
1.08 - Objavljeni znanstveni prispevek na konferenci
Organizacija:
FS - Fakulteta za strojništvo
Opis:
The fatigue strength of polycrystalline metals is hardness and defect size dependent. The fatigue strength of welds depends on the size of grains and actual local mean stress, too. Local mean stress is influenced by the global R-ratio and static preloading. The welds in the as-welded condition are pre-stressed due to the existence of welding residual stresses. The sign and magnitude of residual stresses depend on the welding conditions. Changes of residual stresses, hardness and defect size are experimentally determined in the present work. Samples of studied metals are prepared by using either thermal cycle simulator or laboratory furnace and water quenching. The methods of microstructure preparation and type of load result in actual local R-ratio at the used weld toe models. Specimens are cyclic loaded in the similar way as steel at the weld toe. The bottom of the notch is either defect-free or defected by Vickers indentation. Final results show that coarser grain and higher local R-ratios lower the fatigue strength of welds.
Ključne besede:
CrNiMo steels
,
weld
,
fatigue resistance
,
heat-affected zone
,
small weld defects
Leto izida:
2010
PID:
20.500.12556/DKUM-26738
UDK:
621.791.05:539.431
COBISS.SI-ID:
14779670
ISSN pri članku:
1451-3749
NUK URN:
URN:SI:UM:DK:CUMORRL0
Datum objave v DKUM:
31.05.2012
Število ogledov:
1918
Število prenosov:
35
Metapodatki:
Področja:
Ostalo
Citiraj gradivo
Navadno besedilo
BibTeX
EndNote XML
EndNote/Refer
RIS
ABNT
ACM Ref
AMA
APA
Chicago 17th Author-Date
Harvard
IEEE
ISO 690
MLA
Vancouver
:
Kopiraj citat
Skupna ocena:
(0 glasov)
Vaša ocena:
Ocenjevanje je dovoljeno samo
prijavljenim
uporabnikom.
Objavi na:
Postavite miškin kazalec na naslov za izpis povzetka. Klik na naslov izpiše podrobnosti ali sproži prenos.
Gradivo je del revije
Naslov:
Integritet i vek konstrukcija
Skrajšan naslov:
Integr. vek konstr.
Založnik:
Društvo za integritet i vek konstrukcija.
ISSN:
1451-3749
COBISS.SI-ID:
10931478
Sekundarni jezik
Jezik:
Angleški jezik
Naslov:
Neki faktori koji utiču na otpornost zavara prema zamoru
Ključne besede:
CrNiMo jekla
,
zvar
,
odpornost proti utrujanju
,
toplotno vplivano območje
,
majhne varilne napake