| Naslov: | Microstructure of rapidly solidified Cu-Al-Ni shape memory alloy ribbons |
|---|
| Avtorji: | ID Lojen, Gorazd (Avtor)
ID Anžel, Ivan (Avtor)
ID Kneissl, Albert C. (Avtor)
ID Unterweger, Elfride (Avtor)
ID Kosec, Borut (Avtor)
ID Bizjak, Milan (Avtor) |
|---|
| Datoteke: |  http://dx.doi.org/10.1016/j.jmatprotec.2005.02.196
|
|---|
| Jezik: | Angleški jezik |
|---|
| Vrsta gradiva: | Neznano |
|---|
| Tipologija: | 1.01 - Izvirni znanstveni članek |
|---|
| Organizacija: | FS - Fakulteta za strojništvo
|
|---|
| Opis: | Cu-Al-Ni shape memory alloys (SMAs) are currently the only available high temperature SMAs, showing a good resistance against functional fatigue. In polycrystalline state, they are very brittle and exhibit, in general, only small reversible deformations. By melt spinning, thin Cu-Al-Ni ribbons can be manufactured directly from the melt. Appropriate casting parameters can ensurea single layer columnar structure with a fibre texture, which significantly increases the maximal reversible strain in longitudinal direction. Cu-Al-Ni ribbons, containing 13, 14 and 15 wt.% Al were cast by free jet melt spinning. Because of the alloys' low thermal conductivity, the cooling rate was surprisingly low - considering the crystal grain size - significantly below 103 K/s. Therefore, wide ribbons having a single layer columnar and (except the ribbons containing 13 wt.% Al) completely martensiticstructure could not be obtained. Regardless the chemical composition, the ribbons have a single layer columnar structure only if the thickness does not exceed approximately 50 m, otherwise the structure consists of at least two layers of equiaxed grains. In as-cast condition, only ribbons containing 13 wt.% Al seem to be completely martensitic. Heat treatments at temperatures up to 900 °C improved the structure of 13 and 14 wt.% Al ribbons. All ribbons exhibit one-way shape memory effect in as-cast condition. Heat-treated ribbons containing 13 wt.% Al exhibited two-way shape memory effect already after one bending and heating cycle. |
|---|
| Ključne besede: | metallurgy, shape memory alloys, Cu-Al-Ni alloy, microstructure, melt spinning |
|---|
| Leto izida: | 2005 |
|---|
| PID: | 20.500.12556/DKUM-27025  |
|---|
| UDK: | 669.018 |
|---|
| COBISS.SI-ID: | 9607190 |
|---|
| ISSN pri članku: | 0924-0136 |
|---|
| NUK URN: | URN:SI:UM:DK:SXUPLTDV |
|---|
| Datum objave v DKUM: | 01.06.2012 |
|---|
| Število ogledov: | 2802 |
|---|
| Število prenosov: | 122 |
|---|
| Metapodatki: |    |
|---|
| Področja: | Ostalo
|
|---|
|
:
|
Kopiraj citat |
|---|
| | | | Skupna ocena: | (0 glasov) |
|---|
| Vaša ocena: | Ocenjevanje je dovoljeno samo prijavljenim uporabnikom. |
|---|
| Objavi na: |  |
|---|
Postavite miškin kazalec na naslov za izpis povzetka. Klik na naslov izpiše
podrobnosti ali sproži prenos. |