| Naslov: | The effect of nitrogen-ion implantation on the corrosion resistance of titanium in comparison with oxygen- and argon-ion implantations |
|---|
| Avtorji: | ID Sundararajan, T. (Avtor)
ID Praunseis, Zdravko (Avtor) |
|---|
| Datoteke: |  Materiali_in_tehnologije_2004_Sundararajan,_Praunseis_The_effect_of_nitrogen-ion_implantation_on_the_corrosion_resistance_of_titanium_in.pdf (3,38 MB)
MD5: 9F5A31F9ED0A0F697894EB47E1074121
 http://mit.imt.si/Revija/izvodi/mit0412/sundararajan.pdf
|
|---|
| Jezik: | Angleški jezik |
|---|
| Vrsta gradiva: | Znanstveno delo |
|---|
| Tipologija: | 1.01 - Izvirni znanstveni članek |
|---|
| Organizacija: | FS - Fakulteta za strojništvo
|
|---|
| Opis: | Commercially pure (CP) titanium was surface modified with nitrogen-, argon- and oxygen-ion implantations in order to investigate the material's corrosion resistance in a simulated body fluid. Five doses were chosen for the ions, ranging from 5.1015 cm-2 to 2.5-1017 cm-2. In-vitro open-cyclic potential-timemeasurements and cyclic polarization studies were carried out to evaluate the corrosion resistance of the modified surface in comparison to an unmodified surface. Specimens implanted at 4.1016 cm-2 and 7.1016 cm-2 showed the optimum corrosion resistance, higher doses showed a detrimental effect on the corrosion resistance. Argon- and oxygen-ion implantation at these doses did not show any improved corrosion resistance, indicating the beneficial role of nitrogen on the corrosion resistance of titanium in the simulated body-fluid environment. Grazing-incidence X-ray diffraction (GIXD) was employed on the implanted specimens to determine the phases formed with the increasing doses. X-ray photoelectron spectroscopy (XPS) studies on the passive film of the implanted samples and on the unimplanted samples were analyzed in order to understand the role of nitrogen in improving the corrosion resistance. The results of the present investigation indicated that nitrogen-ion implantation can be used as a viable method for improving the corrosion resistance of titanium. The nature of the surface and the reason for the variation and the improvement in the corrosion resistance are discussed in detail. |
|---|
| Ključne besede: | metallurgy, ion implantation, orthopedic implants, corrosion, titanium, nitrogen, oxygen, argon |
|---|
| Status publikacije: | Objavljeno |
|---|
| Verzija publikacije: | Objavljena publikacija |
|---|
| Leto izida: | 2004 |
|---|
| Št. strani: | str. 19-24 |
|---|
| Številčenje: | Letn. 38, št. 1/2 |
|---|
| PID: | 20.500.12556/DKUM-53073  |
|---|
| ISSN: | 1580-2949 |
|---|
| UDK: | 669.295:617.3:620.193 |
|---|
| COBISS.SI-ID: | 8767254 |
|---|
| ISSN pri članku: | 1580-2949 |
|---|
| NUK URN: | URN:SI:UM:DK:DILBTODA |
|---|
| Datum objave v DKUM: | 10.07.2015 |
|---|
| Število ogledov: | 2682 |
|---|
| Število prenosov: | 112 |
|---|
| Metapodatki: |    |
|---|
| Področja: | Ostalo
|
|---|
|
:
|
Kopiraj citat |
|---|
| | | | Skupna ocena: | (0 glasov) |
|---|
| Vaša ocena: | Ocenjevanje je dovoljeno samo prijavljenim uporabnikom. |
|---|
| Objavi na: |  |
|---|
Postavite miškin kazalec na naslov za izpis povzetka. Klik na naslov izpiše
podrobnosti ali sproži prenos. |