| Naslov: | Mechanical properties and microstructure characterisation of Au-Pt dental alloy |
|---|
| Avtorji: | ID Rudolf, Rebeka (Avtor)
ID Zupančič Hartner, Tjaša (Avtor)
ID Kosec, Ladislav (Avtor)
ID Todorović, Aleksandar (Avtor)
ID Kosec, Borut (Avtor)
ID Anžel, Ivan (Avtor) |
|---|
| Datoteke: |  Metalurgija_2008_Rudolf_et_al._Mechanical_properties_and_microstructure_characterisation_of_Au-Pt_dental_alloy.pdf (1,59 MB)
MD5: 7AEC6EC5836B6DD2B6014C432D442838
PID: 20.500.12556/dkum/0a0f82d3-ac7a-4af9-9763-272cabae1c9c
 http://hrcak.srce.hr/26040
|
|---|
| Jezik: | Angleški jezik |
|---|
| Vrsta gradiva: | Znanstveno delo |
|---|
| Tipologija: | 1.01 - Izvirni znanstveni članek |
|---|
| Organizacija: | FS - Fakulteta za strojništvo
|
|---|
| Opis: | Development of a dental alloy with high Au content is based on the ternary system of Au-Pt-Zn with a nominal composition of 86,9Au-9,9Pt-1,5Zn, and about 1,5 wt.% micro-alloying elements (In, Ir, Rh). The results analyses of different heat-treated states showed that the optimal mechanical properties and hardness of an Au-Pt-Zn alloy can be reached with combinations of heat treatment for 20 minutes at 723 K and then slowly cooling, if the alloy was annealed at 1223 K for 30 minutes and the water quenched. Research results confirmed that the microstructure of the Au-Pt-Zn alloy consists of two phases: α1-phase rich in Au (main phase) and α2-phase rich in Pt (minor phase). During XRD analysis and use of the Rietveld method, it was found that the α1-phase content is about 98,5 wt.% while the content of α2-phase is 1,5 wt.%. STA analyses show that the Au-Pt-Zn alloy has a solidus temperature of about 1292 K and a liquidus temperature of about 1412 K. |
|---|
| Ključne besede: | Au dental alloy, properties, microstructure, characterization |
|---|
| Status publikacije: | Objavljeno |
|---|
| Verzija publikacije: | Objavljena publikacija |
|---|
| Leto izida: | 2008 |
|---|
| Št. strani: | str. 317-323 |
|---|
| Številčenje: | Letn. 47, št. 4 |
|---|
| PID: | 20.500.12556/DKUM-66576  |
|---|
| ISSN: | 1334-2576 |
|---|
| UDK: | 669 |
|---|
| COBISS.SI-ID: | 827487 |
|---|
| ISSN pri članku: | 1334-2576 |
|---|
| NUK URN: | URN:SI:UM:DK:ZO87I0UC |
|---|
| Datum objave v DKUM: | 03.07.2017 |
|---|
| Število ogledov: | 1491 |
|---|
| Število prenosov: | 138 |
|---|
| Metapodatki: |    |
|---|
| Področja: | Ostalo
|
|---|
|
:
|
Kopiraj citat |
|---|
| | | | Skupna ocena: | (0 glasov) |
|---|
| Vaša ocena: | Ocenjevanje je dovoljeno samo prijavljenim uporabnikom. |
|---|
| Objavi na: |  |
|---|
Postavite miškin kazalec na naslov za izpis povzetka. Klik na naslov izpiše
podrobnosti ali sproži prenos. |