| Naslov: | Structural properties and thermal stability of cobalt- and chromium-doped $α-MnO_2$ nanorods |
|---|
| Avtorji: | ID Cerc Korošec, Romana (Avtor)
ID Umek, Polona (Avtor)
ID Gloter, Alexandre (Avtor)
ID Padežnik Gomilšek, Jana (Avtor)
ID Bukovec, Peter (Avtor) |
|---|
| Datoteke: |  Beilstein_Journal_of_Nanotechnology_2017_Cerc_Korosec_et_al._Structural_properties_and_thermal_stability_of_cobalt-_and_chromium-doped_α.pdf (8,24 MB)
MD5: 1711B3579EB146884854FF82B1F131AB
PID: 20.500.12556/dkum/a7c928ee-7bc4-4ff9-ab54-15f374bd7fd2
 http://www.beilstein-journals.org/bjnano/content/8/1/104
|
|---|
| Jezik: | Angleški jezik |
|---|
| Vrsta gradiva: | Znanstveno delo |
|---|
| Tipologija: | 1.01 - Izvirni znanstveni članek |
|---|
| Organizacija: | FS - Fakulteta za strojništvo
|
|---|
| Opis: | $α-MnO_2$ nanorods were synthesized via the hydrothermal decomposition of $KMnO_4$ in an acidic environment in the presence of $Co^{2+}$ and $Cr^{3+}$ ions. Reactions were carried out at three different temperatures: 90, 130 and 170 °C. All prepared samples exhibit a tetragonal $MnO_2$ crystalline phase. SEM–EDS analysis shows that cobalt cations are incorporated to a higher degree into the $MnO_2$ framework than chromium ions, and that the content of the dopant ions decreases with increasing reaction temperature. The oxidation of $Co^{2+}$ to $Co^{3+}$ during the reaction was proved by an XANES study, while EXAFS results confirm that both dopant ions substitute $Mn^{4+}$ in the center of an octahedron. The K/Mn ratio in the doped samples synthesized at 170 °C is significantly lower than in the undoped samples. Analysis of an individual cobalt-doped $α-MnO_2$ nanorod with HAADF-STEM reveals that the distribution of cobalt through the cross-section of the nanorod is uniform. The course of thermal decomposition of the doped nanorods is similar to that of the undoped ones. Dopant ions do not preserve the $MnO_2$ phase at higher temperatures nor do they destabilize the cryptomelane structure. |
|---|
| Ključne besede: | $α-MnO_2$, manganese dioxide, doping, EXAFS, nanorods, XANES |
|---|
| Status publikacije: | Objavljeno |
|---|
| Verzija publikacije: | Objavljena publikacija |
|---|
| Leto izida: | 2017 |
|---|
| Št. strani: | str. 1032-1042 |
|---|
| Številčenje: | Letn. 8 |
|---|
| PID: | 20.500.12556/DKUM-67303  |
|---|
| ISSN: | 2190-4286 |
|---|
| UDK: | 546.711-31:620.3 |
|---|
| COBISS.SI-ID: | 1537419971 |
|---|
| DOI: | 10.3762/bjnano.8.104 |
|---|
| ISSN pri članku: | 2190-4286 |
|---|
| NUK URN: | URN:SI:UM:DK:1M6PJSNJ |
|---|
| Datum objave v DKUM: | 10.08.2017 |
|---|
| Število ogledov: | 1686 |
|---|
| Število prenosov: | 515 |
|---|
| Metapodatki: |    |
|---|
| Področja: | Ostalo
|
|---|
|
:
|
Kopiraj citat |
|---|
| | | | Skupna ocena: | (0 glasov) |
|---|
| Vaša ocena: | Ocenjevanje je dovoljeno samo prijavljenim uporabnikom. |
|---|
| Objavi na: |  |
|---|
Postavite miškin kazalec na naslov za izpis povzetka. Klik na naslov izpiše
podrobnosti ali sproži prenos. |