| Naslov: | Chemical modification and characterization of the surface of polysulfone membranes |
|---|
| Avtorji: | ID Kukovičič, Irena (Avtor)
ID Šoster, Robert (Avtor)
ID Brumen, Milan (Avtor)
ID Ribitsch, Volker (Avtor)
ID Wiegel, D. (Avtor)
ID Arnold, K. (Avtor)
ID Stropnik, Črtomir (Avtor) |
|---|
| Datoteke: |  Acta_Chimica_Slovenica_2000_Kukovicic_et_al._Chemical_Modification_and_Characterization_of_the_surface_of_polysulfone_membranes.pdf (82,15 KB)
MD5: 3357E90B998C5322265A180966434A93
PID: 20.500.12556/dkum/edaa0857-5751-4623-adb6-ce0bb1196761
 http://acta-arhiv.chem-soc.si/47/47-3-339.pdf
|
|---|
| Jezik: | Angleški jezik |
|---|
| Vrsta gradiva: | Znanstveno delo |
|---|
| Tipologija: | 1.01 - Izvirni znanstveni članek |
|---|
| Organizacija: | FKKT - Fakulteta za kemijo in kemijsko tehnologijo
|
|---|
| Opis: | Asymmetric porous membranes were prepared from polysulfone by a wet-phase separation procedure. Different chemical modifications were applied to the upper membrane surface, i.e. the surface which was exposed to interaction with nonsolvent (water) in the coagulation bath during the membrane formation. The membrane surface was modified by the series of Friedel-Crafts electrophilic substitutions of aromatic rings in the polysulfone molecules. As a reagent 1-chlorodecane or propylene oxide dissolved in hexane and $AlCl_3$ as a catalyst were used. In the former case a hydrophobic and in the latter one a hydrophilic coating was achieved, respectively. The membrane surface was also modified by sulfonization with sulfuric (VI) acid water solution; in this way negative charges were introduced at the membrane surface. The membranes, unmodified and chemically modified, were characterized by measuring the membrane thickness, the deionized water flux through the membrane, the zeta potential and contact angle. The specific chemical modifications of the membrane surface affect the water flux, the zeta potential and contact angle values whereas the membrane thickness remains unchanged. These effects are interpreted in terms of hydrophilicity and hydrophobicity, changes of the membrane surface charge and the thickness of shear layer at the membrane surface, all with respect to the particular modification applied. Reaction with 1-chlorodecane gave a hydrophobic surface by nonpolar $–(CH_2)_9-CH_3$ groups and reaction with propylene oxide gave a hydrophilic surface with polar group $-CH(CH_3)-CH_2-OH$. The surface of sulfonized polysulfone membranes contained ionizable ($-SO_3H$) functional groups. |
|---|
| Ključne besede: | polysulfone, chemical modification, Friedel-Crafts electrophilic substitution, sulfonization, hydrophylicity, hydrophobicity |
|---|
| Status publikacije: | Objavljeno |
|---|
| Verzija publikacije: | Objavljena publikacija |
|---|
| Leto izida: | 2000 |
|---|
| Št. strani: | str. 339-347 |
|---|
| Številčenje: | Letn. 47, št. 3 |
|---|
| PID: | 20.500.12556/DKUM-67420  |
|---|
| ISSN: | 1318-0207 |
|---|
| UDK: | 541.64.057:577.352:616.15 |
|---|
| COBISS.SI-ID: | 22651653 |
|---|
| ISSN pri članku: | 1318-0207 |
|---|
| NUK URN: | URN:SI:UM:DK:LOCTOWFV |
|---|
| Datum objave v DKUM: | 17.08.2017 |
|---|
| Število ogledov: | 1639 |
|---|
| Število prenosov: | 134 |
|---|
| Metapodatki: |    |
|---|
| Področja: | Ostalo
|
|---|
|
:
|
Kopiraj citat |
|---|
| | | | Skupna ocena: | (0 glasov) |
|---|
| Vaša ocena: | Ocenjevanje je dovoljeno samo prijavljenim uporabnikom. |
|---|
| Objavi na: |  |
|---|
Postavite miškin kazalec na naslov za izpis povzetka. Klik na naslov izpiše
podrobnosti ali sproži prenos. |