| Naslov: | The influence of the ratio of circumference to cross-sectional area of tensile bars on the fatigue life of additive manufactured AISI 316L steel |
|---|
| Avtorji: | ID Ferlič, Luka (Avtor)
ID Jerenec, Filip (Avtor)
ID Šercer, Mario (Avtor)
ID Drstvenšek, Igor (Avtor)
ID Gubeljak, Nenad (Avtor) |
|---|
| Datoteke: |  metals-14-01246-v2.pdf (33,45 MB)
MD5: 4180100B6BDFB43B3E79EBEA48E1C43A
 https://www.mdpi.com/2075-4701/14/11/1246
|
|---|
| Jezik: | Angleški jezik |
|---|
| Vrsta gradiva: | Članek v reviji |
|---|
| Tipologija: | 1.01 - Izvirni znanstveni članek |
|---|
| Organizacija: | FS - Fakulteta za strojništvo
|
|---|
| Opis: | The static and dynamic loading capacities of components depend on the stress level to which the material is exposed. The fatigue behavior of materials manufactured using additive technology is accompanied by a pronounced scatter between the number of cycles at the same stress level, which is significantly greater than the scatter from a material with the same chemical composition, e.g., AISI 316L, but produced by rolling or forging. An important reason lies in the fact that fatigue cracks are initiated almost always below the material surface of the loaded specimen. Thus, in the article, assuming that a crack will always initiate below the surface, we analyzed the fatigue behavior of specimens with the same bearing cross section but with a different number of bearing rods. With a larger number of rods, the circumference around the supporting part of the rods was 1.73 times larger. Thus, experimental fatigue of specimens with different sizes showed that the dynamic loading capacity of components with a smaller number of bars is significantly greater and can be monitored by individual stress levels. Although there are no significant differences in loading capacity under static and low-cycle loading of materials manufactured with additive technologies, in high-cycle fatigue it has been shown that the ratio between the circumference and the loading cross section of tensile-loaded rods plays an important role in the lifetime. This finding is important for setting a strategy for manufacturing components with additive technologies. It shows that a better dynamic loading capacity can be obtained with a larger loading cross section. |
|---|
| Ključne besede: | AISI 316L stainless steel, additive manufacturing, FEM, high-cycle fatigue, fractography analysis |
|---|
| Status publikacije: | Objavljeno |
|---|
| Verzija publikacije: | Objavljena publikacija |
|---|
| Poslano v recenzijo: | 20.09.2024 |
|---|
| Datum sprejetja članka: | 24.10.2024 |
|---|
| Datum objave: | 02.11.2024 |
|---|
| Založnik: | MDPI |
|---|
| Leto izida: | 2024 |
|---|
| Št. strani: | 28 str. |
|---|
| Številčenje: | Vol. 14, iss. 11, [article no.] 1246 |
|---|
| PID: | 20.500.12556/DKUM-91178  |
|---|
| UDK: | 620.178.3 |
|---|
| COBISS.SI-ID: | 214295555 |
|---|
| DOI: | 10.3390/met14111246 |
|---|
| ISSN pri članku: | 2075-4701 |
|---|
| Avtorske pravice: | © 2024 by the authors |
|---|
| Datum objave v DKUM: | 25.11.2024 |
|---|
| Število ogledov: | 192 |
|---|
| Število prenosov: | 32 |
|---|
| Metapodatki: |    |
|---|
| Področja: | Ostalo
|
|---|
|
:
|
Kopiraj citat |
|---|
| | | | Skupna ocena: | (0 glasov) |
|---|
| Vaša ocena: | Ocenjevanje je dovoljeno samo prijavljenim uporabnikom. |
|---|
| Objavi na: |  |
|---|
Postavite miškin kazalec na naslov za izpis povzetka. Klik na naslov izpiše
podrobnosti ali sproži prenos. |