| Naslov: | Synergic effect of large MXene nanosheets and protective coatings on improved electroconductivity and wash durability of MXene/polymer-modified cotton fabric |
|---|
| Avtorji: | ID Jug, Laura (Avtor)
ID Hribernik, Silvo (Avtor)
ID Ojstršek, Alenka (Avtor) |
|---|
| Datoteke: |  1-s2.0-S0300944025000116-main.pdf (8,43 MB)
MD5: 0D7F793E3B0D861F0E9183A91F31FD5D
 https://www.sciencedirect.com/science/article/pii/S0300944025000116?via%3Dihub
|
|---|
| Jezik: | Angleški jezik |
|---|
| Vrsta gradiva: | Članek v reviji |
|---|
| Tipologija: | 1.01 - Izvirni znanstveni članek |
|---|
| Organizacija: | FS - Fakulteta za strojništvo
|
|---|
| Opis: | E-textiles and their wearable analogues are finding applications in a myriad of sectors, ranging from sensors to health and sports applications. The development of a truly functional and reusable textile substrate presents a challenging task; its design encompasses the fabrication of optimal functional conductive particles, as well as devising strategies for their application that will ensure their functional properties (e.g. conductivity) are retained in an undiminished state for a foreseeable period. In the presented study, we tackled these two aspects in an interdependent way: i) The enhancement of the electrical conductivity of MXene-modified cotton fabric by increasing the lateral size of nanosheets during the Ti3C2TX synthesis, and ii) The improvement of washing durability of MXenes on the fabric surface by selecting suitable protective coatings. The results of Scanning Electron Microscopy (SEM), X-ray powder Diffraction (XRD), Dynamic Light Scattering (DLS) and Atomic Force Microscopy (AFM) revealed the successful synthesis of large and stable MXene nanosheets with ultrathin flakelike nanostructures, high colloidal stability and delamination yields. Using multiple application procedures of dipping and drying, the MXene nanosheets formed extensive adhesion areas on the cotton fabric and overlapped the fibre pores, thus reducing the interfacial resistance between the sheets and improving the coating uniformity and, consequently, increasing electrical conductivity. Weaker adhesion and depletion of large nanosheets were further effectively prevented by protective polymer coatings. The MXene-coated/protected fabrics had sufficient electrical conductivity, even after 20 laundering cycles. Moreover, the surface hydrophobicity was negligibly reduced, preventing water accessibility and, thus, increasing the oxidation stability of the applied MXenes. |
|---|
| Ključne besede: | Ti3C2TX MXene, synthesis parameters, cotton fabric, electrical conductivity, protective coatings, washing durability |
|---|
| Status publikacije: | Objavljeno |
|---|
| Verzija publikacije: | Objavljena publikacija |
|---|
| Poslano v recenzijo: | 02.01.2025 |
|---|
| Datum sprejetja članka: | 09.01.2025 |
|---|
| Datum objave: | 19.01.2025 |
|---|
| Založnik: | Elsevier |
|---|
| Leto izida: | 2025 |
|---|
| Št. strani: | 13 str. |
|---|
| Številčenje: | Vol. 200, [article no.] 109062 |
|---|
| PID: | 20.500.12556/DKUM-91997  |
|---|
| UDK: | 677.017 |
|---|
| COBISS.SI-ID: | 224073475 |
|---|
| DOI: | 10.1016/j.porgcoat.2025.109062 |
|---|
| ISSN pri članku: | 1873-331X |
|---|
| Datum objave v DKUM: | 10.03.2025 |
|---|
| Število ogledov: | 284 |
|---|
| Število prenosov: | 24 |
|---|
| Metapodatki: |    |
|---|
| Področja: | Ostalo
|
|---|
|
:
|
Kopiraj citat |
|---|
| | | | Skupna ocena: | (0 glasov) |
|---|
| Vaša ocena: | Ocenjevanje je dovoljeno samo prijavljenim uporabnikom. |
|---|
| Objavi na: |  |
|---|
Postavite miškin kazalec na naslov za izpis povzetka. Klik na naslov izpiše
podrobnosti ali sproži prenos. |